Composition and method for polishing memory hard disks exhibiting reduced edge roll off

ABSTRACT

The invention provides a chemical-mechanical polishing composition comprising (a) an abrasive comprising colloidal silica and fused silica, (b) a compound of formula (I) or a combination of a compound of formula (II) and a hydrophobic organic compound, (c) an amino acid, (d) hydrogen peroxide, and (e) water, wherein the polishing composition has a pH of about 1 to about 5. The invention also provides a method of chemically-mechanically polishing a substrate, especially a nickel-phosphorous substrate, by contacting the substrate with the inventive chemical-mechanical polishing composition.

BACKGROUND OF THE INVENTION

The demand for increased storage capacity in memory or rigid disks and the trend towards miniaturization of memory or rigid disks (e.g., due to the requirement for smaller hard drives in computer equipment) continues to emphasize the importance of the memory or rigid disk manufacturing process, including the planarization or polishing of such disks for ensuring maximal performance. While there exist several chemical-mechanical polishing (CMP) compositions and methods for use in conjunction with semiconductor device manufacture, few conventional CMP methods or commercially available CMP compositions are well-suited for the planarization or polishing of memory or rigid disks.

As the demand for greater storage capacity has increased, so has the need for improved processes for the polishing of such memory or rigid disks. The term “memory or rigid disk” refers to any magnetic disk, hard disk, rigid disk, or memory disk for retaining information in electromagnetic form. The memory or rigid disk typically has a surface that comprises nickel-phosphorus, but the memory or rigid disk surface can comprise any other suitable material. The planarity of the memory or rigid disks must be improved, as the distance between the recording head of a disk drive and the surface of the memory or rigid disk has decreased with improvements in recording density that demand a lower flying height of the magnetic head with respect to the memory or rigid disk. In order to permit a lower flying height of the magnetic head, improvements to the surface finish of the memory or rigid disk are required.

During the polishing of a memory or rigid disk, typically the edges of the disk receive a higher pressure from the polishing tool than the remaining surface area of the disk. Typically, polishing is performed using a combination of an abrasive, a polishing pad, and a liquid carrier, in which the abrasive may be suspended in the liquid carrier, or may be affixed to the surface of the pad. As the polishing process mainly consists of mechanical abrasion of the disk by the abrasive and/or pad, in conjunction with the action of chemicals that may be present, and the rate of abrasion is at least in part a function of pressure applied, the edges of the disk experience a higher rate of abrasion than the rest of the disk. This leads to the formation of a curved, or rounded, contour at the edges of the disk, known in the art as edge roll-off, rub-off, or dub-off. Such rounded areas on a disk are unsuitable for recording. Thus, if the amount of roll-off can be reduced, the recording capacity for a disk can be increased.

Thus, there remains in the art a need for chemical-mechanical polishing compositions for memory or rigid disks that exhibit satisfactory nickel-phosphorous removal rates while minimizing the amount of roll-off resulting from polishing.

BRIEF SUMMARY OF THE INVENTION

The invention provides a chemical-mechanical polishing composition comprising (a) an abrasive comprising colloidal silica and fused silica, (b) about 10 ppm to about 1000 ppm of a compound of formula (I):

wherein R is selected from

a straight chain or branched chain C₁-C₂₀ alkyl,

and

R⁵C₆H₄, and

R⁶—O—(R⁷O)_(n)—,

wherein R¹-R⁵ are independently selected from straight chain or branched chain C₁-C₂₀ alkyls,

wherein R⁶ is a straight chain or branched chain C₁-C₂₀ alkyl or R⁸—C₆H₄—,

wherein R⁷ is a straight chain or branched chain C₂-C₁₀ alkylene,

wherein R⁸ is a straight chain or branched chain C₁-C₂₀ alkyl,

wherein n is an integer of from 1 to about 20,

wherein X and Y are independently O or a covalent bond, and

wherein A and B are independently an alkali metal cation or an organic amine compound, (c) an amino acid, (d) hydrogen peroxide, and (e) water, wherein the polishing composition has a pH of about 1 to about 5.

The invention also provides a chemical-mechanical polishing composition comprising (a) an abrasive comprising colloidal silica and fused silica, (b) a compound of formula (II):

wherein R⁹ is H or a hydroxyalkyl, and wherein m is an integer of from 2 to about 6, (c) a hydrophobic organic compound selected from an aryloxy alcohol, a diester, and a triester, (d) hydrogen peroxide, (e) an amino acid, and (f) water, wherein the polishing composition has a pH of about 1 to about 5.

The invention further provides a method of chemically mechanically polishing a substrate comprising (i) providing a substrate, (ii) providing a polishing pad, (iii) providing a chemical-mechanical polishing composition comprising (a) an abrasive comprising colloidal silica and fused silica, (b) about 10 ppm to about 1000 ppm of a compound of formula (I):

wherein R is selected from

a straight chain or branched chain C₁-C₂₀ alkyl,

and

R⁵C₆H₄, and

R⁶—O—(R⁷O)_(n)—,

wherein R¹-R⁵ are independently selected from straight chain or branched chain C₁-C₂₀ alkyls,

wherein R⁶ is a straight or branched chain C₁-C₂₀ alkyl or R⁸—C₆H₄—,

wherein R⁷ is a straight or branched chain C₂-C₁₀ alkylene,

wherein R⁹ is a straight or branched chain C₁-C₂₀ alkyl,

wherein n is an integer of from 1 to about 20,

wherein X and Y are independently O or a covalent bond, and

wherein A and B are independently an alkali metal cation or an organic amine compound, (c) an amino acid, (d) hydrogen peroxide, and (e) water, wherein the polishing composition has a pH of about 1 to about 5, (iv) contacting the substrate with the polishing pad and the chemical-mechanical polishing composition, and (v) moving the polishing pad and the chemical mechanical polishing composition relative to the substrate to abrade at least a portion of a surface of the substrate to thereby polish the substrate.

The invention additionally provides a method of chemically mechanically polishing a substrate comprising (i) providing a substrate, (ii) providing a polishing pad, (iii) providing a chemical-mechanical polishing composition comprising (a) an abrasive comprising colloidal silica and fused silica, (b) a compound of formula (II):

wherein R⁹ is H or a hydroxyalkyl, and wherein m is an integer of from 2 to about 6, (c) a hydrophobic organic compound selected from an aryloxy alcohol, a diester, and a triester, (d) hydrogen peroxide, (e) an amino acid, and (f) water, wherein the polishing composition has a pH of about 1 to about 5, (iv) contacting the substrate with the polishing pad and the chemical-mechanical polishing composition, and (v) moving the polishing pad and the chemical mechanical polishing composition relative to the substrate to abrade at least a portion of a surface of the substrate to thereby polish the substrate.

DETAILED DESCRIPTION OF THE INVENTION

In an embodiment, the invention provides a chemical-mechanical polishing composition comprising, consisting essentially of, or consisting of (a) an abrasive comprising colloidal silica and fused silica, (b) about 10 ppm to about 1000 ppm of a compound of formula (I):

wherein R is selected from

a straight chain or branched chain C₁-C₂₀ alkyl,

and

R⁵C₆H₄, and

R⁶—O—(R⁷O)_(n)—,

wherein R¹-R⁵ are independently selected from straight chain or branched chain C₁-C₂₀ alkyls,

wherein R⁶ is a straight chain or branched chain C₁-C₂₀ alkyl or R⁸—C₆H₄—,

wherein R⁷ is a straight chain or branched chain C₂-C₁₀ alkylene,

wherein R⁹ is a straight chain or branched chain C₁-C₂₀ alkyl,

wherein n is an integer of from 1 to about 20,

wherein X and Y are independently O or a covalent bond, and

wherein A and B are independently an alkali metal cation or an organic amine compound, (c) an amino acid, (d) hydrogen peroxide, and (e) water, wherein the polishing composition has a pH of about 1 to about 5.

The invention also provides a chemical-mechanical polishing composition comprising, consisting essentially of, or consisting of (a) an abrasive comprising colloidal silica and fused silica, (b) a compound of formula (II):

wherein R⁹ is H or a hydroxyalkyl, and wherein m is an integer of from 2 to about 6, (c) a hydrophobic organic compound selected from an aryloxy alcohol, a diester, and a triester, (d) hydrogen peroxide, (e) an amino acid, and (f) water, wherein the polishing composition has a pH of about 1 to about 5.

The chemical-mechanical polishing composition includes an abrasive that comprises, consists essentially of, or consists of a combination of colloidal silica and fused silica. The abrasive can comprise any suitable relative proportion of colloidal silica to fused silica. For example, the abrasive can include about 50% to about 90% of colloidal silica and about 10% to about 50% of fused silica, relative to the total amount of the combination of colloidal silica and fused silica.

The colloidal silica can be any suitable colloidal silica. For example, the colloidal silica can be a wet process silica, such as a condensation-polymerized silica. Condensation-polymerized silica typically is prepared by condensing Si(OH)₄ to form colloidal particles, where colloidal is defined as having an average particle size between about 1 nm and about 1000 nm. Such abrasive particles can be prepared in accordance with U.S. Pat. No. 5,230,833 or can be obtained as any of various commercially available products, such as the Akzo-Nobel Bindzil™ 50/80, 30/360, 159/500, 40/220, and 40/130 products and the Nalco 1050, 1060, 2327, and 2329 products, as well as other similar products available from DuPont, Bayer, Applied Research, Nissan Chemical, Fuso, and Clariant.

The colloidal silica can have any suitable average particle size (i.e., average particle diameter). The particle size of an abrasive particle is the diameter of the smallest sphere that encompasses the abrasive particle. The colloidal silica can have an average particle size of about 5 nm or more, e.g., about 10 nm or more, about 15 nm or more, about 20 nm or more, about 25 nm or more, about 30 nm or more, about 35 nm or more, or about 40 nm or more. Alternatively, or in addition, the colloidal silica can have an average particle size of about 200 nm or less, e.g., about 190 nm or less, about 180 nm or less, about 170 nm or less, about 160 nm or less, or about 150 nm or less. Thus, the colloidal silica can have an average particle size bounded by any two of the aforementioned endpoints. For example, the colloidal silica can have an average particle size of about 5 nm to about 200 nm, e.g., about 10 nm to about 200 nm, about 10 nm to about 190 nm, about 20 nm to about 180 nm, about 20 nm to about 170 nm, about 20 nm to about 160 nm, about 20 nm to about 150 nm, about 30 nm to about 150 nm, or about 40 nm to about 150 nm.

In some embodiments, the polishing composition can comprise two or more different colloidal silicas. The two or more different colloidal silicas can have the same or different average particle sizes, provided that each of the two or more different colloidal silicas has an average particle size as set forth herein.

The fused silica can be any suitable fused silica. Fused silica is a distinctly different material than colloidal silica or fumed silica, and has, for example, different chemical and physical properties compared to colloidal silica and fumed silica, including different polishing characteristics. Colloidal silica typically is manufactured in solution in a wet process, as described above. The hydrolysis conditions result in distinct particle size distributions and particle morphology, as typically spherical or spheroidal particles. Fumed silica is produced by pyrolysis of a precursor such as a silicon tetrachloride, and condensation from the gas phase. Fumed silica consists of nanometer to micron-sized particles of amorphous silica having branched, chain-like, three-dimensional secondary particles which then agglomerate into tertiary particles, and has low bulk density and high surface area. In contrast, fused silica is a glass that is produced at high temperatures from, e.g., silicon, by oxidation and fusion, typically followed by comminution and/or sieving to produce a fine powder. Fused silica, like fumed silica, has a substantially fully condensed surface having little or no SiOH groups as compared to colloidal silica, which has a substantial amount of hydroxyl functionality on the particle surface.

In some embodiments, the particle morphology of fused silica can be more like the typical spherical or spheroidal particles of colloidal silica rather than the typical aggregated particles of fumed silica. In addition, fused silica has a higher true density than either colloidal silica or fumed silica. The isoelectric point of fused silica is around zero.

In certain embodiments, the particle morphology of the fused silica is highly irregular-shaped, for example, as described in co-pending U.S. patent application Ser. No. 15/951,358, the disclosure of which is incorporated herein by reference. In these embodiments, highly irregular-shaped fused silica comprises particles which may be distinguished from fused silica comprising spherical or spheroidal particles. As used herein, the terms “spherical or spheroidal particles” refer to particles that are essentially entirely rounded over their surfaces and appear (e.g., in a photomicrograph) to be relatively smooth, meaning that the particles are substantially rounded, curved, and smooth, in their cross-sectional shape in three (orthogonal) dimensions.

As opposed to spherical or spheroidal fused silica, highly irregular-shaped fused silica, as the term is used herein, comprises particles that are different from spherical or spheroidal particles, and that as a collection of particles exhibit varied forms and differing shapes and geometries, including a substantial amount of asymmetry. As opposed to entirely spherical or spheroidal surfaces and mostly symmetric cross-sections, the highly irregular-shaped particles include particles that exhibit a substantial amount of cross-sectional asymmetry, e.g., that have substantial portions of their surfaces and edges that (when viewed in a photomicrograph) are flat, bumpy, angled (angular or cornered), rough, or irregular, with flat, jagged, angled, or fractured surface features and non-rounded (e.g., linear, jagged, angular, rough, or cornered) edges of the surfaces, including particles that include a substantial or a high amount (proportionally) of non-rounded, rough, jagged, or fractured surfaces and edges.

The fused silica can have any suitable average particle size (i.e., average particle diameter). The fused silica can have an average particle size of about 10 nm or more, e.g., about 20 nm or more, about 30 nm or more, about 40 nm or more, about 50 nm or more, about 60 nm or more, about 70 nm or more, about 80 nm or more, about 90 nm or more, or about 100 nm or more. Alternatively, or in addition, the fused silica can have an average particle size of about 1000 nm or less, e.g., about 950 nm or less, about 900 nm or less, about 850 nm or less, about 800 nm or less, about 750 nm or less, about 700 nm or less, about 650 nm or less, about 600 nm or less, about 550 nm or less, or about 500 nm or less. Thus, the fused silica can have an average particle size bounded by any two of the aforementioned endpoints. For example, the fused silica can have an average particle size of about 10 nm to about 1000 nm, e.g., about 20 nm to about 900 nm, about 30 nm to about 800 nm, about 40 nm to about 700 nm, about 50 nm to about 600 nm, about 70 nm to about 600 nm, about 80 nm to about 600 nm, about 90 nm to about 600 nm, or about 100 nm to about 800 nm.

The polishing composition can comprise any suitable amount of a combination of colloidal silica and fused silica. Typically, the polishing composition can comprise about 0.1 wt. % or more of a combination of colloidal silica and fused silica, e.g., about 0.2 wt. % or more, about 0.4 wt. % or more, about 0.6 wt. % or more, about 0.8 wt. % or more, or about 1 wt. % or more. Alternatively, or in addition, the polishing composition can comprise about 10 wt. % or less of a combination of colloidal silica and fused silica, e.g., about 9 wt. % or less, about 8 wt. % or less, about 7 wt. % or less, about 6 wt. % or less, or about 5 wt. % or less. Thus, the polishing composition can comprise a combination of colloidal silica and fused silica in an amount bounded by any two of the aforementioned endpoints. For example, the polishing composition can comprise about 0.1 wt. % to about 10 wt. % of a combination of colloidal silica and fused silica, e.g., about 0.2 wt. % to about 10 wt. %, about 0.4 wt. % to about 9 wt. %, about 0.6 wt. % to about 8 wt. %, about 0.8 wt. % to about 7 wt. %, about 1 wt. % to about 6 wt. %, or about 1 wt. % to about 5 wt. %.

The abrasive comprising colloidal silica and fused silica preferably is colloidally stable. The term colloid refers to the suspension of abrasive particles in the liquid carrier. Colloidal stability refers to the maintenance of that suspension through time. In the context of the invention, an abrasive is considered colloidally stable if, when the abrasive is placed into a 100 ml graduated cylinder and allowed to stand unagitated for a time of 2 hours, the difference between the concentration of particles in the bottom 50 ml of the graduated cylinder ([B] in terms of g/ml) and the concentration of particles in the top 50 ml of the graduated cylinder ([T] in terms of g/ml) divided by the initial concentration of particles in the abrasive composition ([C] in terms of g/ml) is less than or equal to 0.5 (i.e., {[B]−[T]}/[C]<0.5). More preferably, the value of [B]−[T]/[C] is less than or equal to 0.3, and most preferably is less than or equal to 0.1.

In certain embodiments, the polishing composition comprises a compound of formula (I):

wherein R is selected from

straight or branched chain C₁-C₂₀ alkyl,

and

R⁵C₆H₄, and

R⁶—O—(R⁷O)_(n)—,

wherein R¹-R⁵ are independently selected from straight chain or branched chain C₁-C₂₀ alkyls,

wherein R⁶ is a straight chain or branched chain C₁-C₂₀ alkyl or R⁸—C₆H₄—,

wherein R⁷ is a straight chain or branched chain C₂-C₁₀ alkylene,

wherein R⁸ is a straight chain or branched chain C₁-C₂₀ alkyl,

wherein n is an integer of from 1 to about 20,

wherein X and Y are independently O or a covalent bond, and

wherein A and B are independently an alkali metal cation or an organic amine compound.

Non-limiting examples of the compound of formula (I) wherein R is a straight chain or branched chain C₁-C₂₀ alkyl and wherein X is O include alkyl sulfates such as CH₃(CH₂)₉SO₃H, CH₃(CH₂)₁₁SO₃H, CH₃(CH₂)₁₃SO₃H, CH₃(CH₂)₁₅SO₃H, CH₃(CH₂)₁₇SO₃H, and CH₃(CH₂)₁₉SO₃H, sodium salts thereof, and organic amine salts thereof.

Non-limiting examples of the compound of formula (I) wherein R is a branched chain C₁-C₂₀ alkyl and X is a covalent bond include secondary alkyl sulfonates, for example, wherein R is a secondary C₁₃-C₁₈ branched chain alkyl group, such as the compounds having CAS Registry Numbers 68037-49-0, 68188-18-1, and 97489-15-1.

Non-limiting examples of the compound of formula (I) wherein R is

X is a covalent bond, and R¹ and R² are both ethyl hexyl include diethylhexyl sulfosuccinate, sodium salts thereof, and organic amine salts thereof.

Non-limiting examples of the compound of formula (I) wherein R is R⁵C₆H₄ and X is a covalent bond include linear alkyl benzenesulfonates such as dodecyl benzenesulfonate, and other alkyl benzenesulfonates such as sec-alkyl derivatives thereof, for example, a benzenesulfonic acid C₁₀-C₁₃ sec-alkyl derivative, sodium salts thereof, and organic amine salts thereof, such as isopropylamine salts.

Non-limiting examples of the compound of formula (I) wherein R is

and X and Y are both a covalent bond include diphenyloxide disulfonates, alkylated derivatives thereof (i.e., alkyl diphenyloxide disulfonates) such as diphenyloxide disulfonate C₁₀-alkyl and C₁₂-alkyl derivatives, sodium salts thereof, and organic amine salts thereof. Examples of suitable diphenyloxide disulfonates include the Dowfax™ surfactants (Dow Chemical Co., Midland, Mich.) including Dowfax™ C10L.

Non-limiting examples of the compound of formula (I) wherein R is R⁶—O—(R⁷O)_(n)— and R⁶ is straight or branched chain C₁-C₂₀ alkyl include mono alkyl branched propoxy sulfates such as alkyl (poly)propoxysulfates. A non-limiting example of the compound of formula (I) wherein R is R⁶—O—(R⁷O)_(n)— and R⁶ is R⁸—C₆H₄— is polyethyleneglycol nonylphenyl ether sulfate.

In the compound of formula (I), A and B are independently an alkali metal cation or an organic amine. The alkali metal cation can be any suitable alkali metal cation and is not particularly limited. For example, the alkali metal cation can be lithium ion, sodium ion, potassium ion, rubidium ion, or cesium ion. The organic amine can be any suitable amine and is not particularly limited. For example, the organic amine can be a primary amine (e.g., isopropylamine), a secondary amine (e.g., diethylamine or dibutylamine), or a tertiary amine (e.g., triethylamine), and the like. When A and/or B is an organic amine, it will be understood by those of ordinary skill in the art that the compound of formula (I) is a salt of the organic amine.

The polishing composition can comprise any suitable amount of the compound of formula (I). Typically, the polishing composition comprises about 10 ppm or more of the compound of formula (I), e.g., about 20 ppm or more, about 30 ppm or more, about 40 ppm or more, about 50 ppm or more, about 60 ppm or more, about 70 ppm or more, about 80 ppm or more, about 90 ppm or more, or about 100 ppm or more. Alternatively, or in addition, the polishing composition comprises about 1000 ppm or less of the compound of formula (I), e.g., about 900 ppm or less, about 800 ppm or less, about 700 ppm or less, about 600 ppm or less, about 500 ppm or less, or about 400 ppm or less. Thus, the polishing composition can comprise the compound of formula (I) in an amount bounded by any two of the aforementioned endpoints. For example, the polishing composition can comprise about 10 ppm to about 1000 ppm of the compound of formula (I), e.g., about 20 ppm to about 900 ppm, about 30 ppm to about 800 ppm, about 40 ppm to about 700 ppm, about 50 ppm to about 600 ppm, about 60 ppm to about 500 ppm, about 70 ppm to about 500 ppm, about 80 ppm to about 500 ppm, about 90 ppm to about 500 ppm, about 100 ppm to about 500 ppm, about 150 ppm to about 500 ppm, or about 200 ppm to about 500 ppm. Preferably, the polishing composition comprises about 100 ppm to about 500 ppm of the compound of Formula (I).

In other embodiments, the polishing composition comprises combination of a compound of formula (II):

wherein R⁹ is H or a hydroxyalkyl, and wherein m is an integer of from 2 to about 6, and a hydrophobic organic compound selected from an aryloxy alcohol, a diester, and a triester.

A non-limiting example of the compound of formula (II) wherein R⁶ is H is ethylenediamine. A non-limiting example of the compound of formula (II) wherein R⁶ is hydroxyalkyl is hydroxyethylethylenediamine.

The polishing composition can comprise any suitable amount of the combination of the compound of formula (II) and the hydrophobic organic compound. Typically, the polishing composition comprises about 100 ppm or more of the combination of the compound of formula (II) and the hydrophobic organic compound, e.g., about 150 ppm or more, about 200 ppm or more, about 400 ppm or more, about 600 ppm or more, about 800 ppm or more, or about 1000 ppm or more. Alternatively, or in addition, the polishing composition comprises about 4000 ppm or less of the combination of the compound of formula (II) and the hydrophobic organic compound, e.g., about 3800 ppm or less, about 3600 ppm or less, about 3400 ppm or less, about 3200 ppm or less, about 3000 ppm or less, about 2800 ppm or less, about 2600 ppm or less, about 2400 ppm or less, about 2200 ppm or less, or about 2000 ppm or less. Thus, the polishing composition can comprise the combination of the compound of formula (II) and the hydrophobic organic compound in an amount bounded by any two of the aforementioned endpoints. For example, the polishing composition can comprise about 100 ppm to about 4000 ppm of the compound of formula (II) and the hydrophobic organic compound, e.g., about 200 ppm to about 4000 ppm, about 400 ppm to about 4000 ppm, about 600 ppm to about 4000 ppm, about 600 ppm to about 3800 ppm, about 600 ppm to about 3600 ppm, about 600 ppm to about 3400 ppm, about 600 ppm to about 3200 ppm, about 600 ppm to about 3000 ppm, about 800 ppm to about 3000 ppm, or about 1000 ppm to about 3000 ppm.

The hydrophobic organic compound can be any suitable aryloxy alcohol, diester or triester. A non-limiting example of a suitable aryloxy alcohol is phenoxyethanol. A non-limiting example of a suitable triester is triethyl citrate.

The polishing composition comprises an amino acid. The amino acid can be any suitable amino acid. Non-limiting examples of suitable amino acids include glycine, alanine, lysine, and arginine. The polishing composition can contain any suitable amount of amino acid. For example, the polishing composition can comprise about 0.1 wt. % to about 5 wt. % of amino acid, e.g., about 0.1 wt. % to about 4 wt. %, about 0.1 wt. % to about 3 wt. %, about 0.1 wt. % to about 2 wt. %, or about 0.1 wt. % to about 1 wt. %.

The polishing composition comprises hydrogen peroxide. The hydrogen peroxide can be present in any suitable amount in the polishing composition. For example, the polishing composition can comprise about 0.1 wt. % to about 10 wt. % of hydrogen peroxide, e.g., about 0.5 wt. % to about 10 wt. %, about 0.5 wt. % to about 5 wt. %, about 0.1 wt. % to about 5 wt. %, about 0.1 wt. % to about 2.5 wt. %, or about 0.1 wt. % to about 1 wt. %.

The polishing composition comprises water. The water can be any suitable water and can be, for example, deionized water or distilled water. In some embodiments, the polishing composition can further comprise one or more organic solvents in combination with the water. For example, the polishing composition can further comprise a hydroxylic solvent such as methanol or ethanol, a ketonic solvent, an amide solvent, a sulfoxide solvent, and the like. Preferably, the polishing composition comprises pure water.

The polishing composition can have any suitable pH. Typically, the polishing composition can have a pH of about 1 or more, e.g., about 1.2 or more, about 1.4 or more, about 1.6 or more, about 1.8 or more, or about 2 or more. Alternatively, or in addition, the polishing composition can have a pH of about 5 or less, e.g., about 4.5 or less, about 4 or less, about 3.5 or less, or about 3 or less. Thus, the polishing composition can have a pH bounded by any two of the aforementioned endpoints. For example, the polishing composition can have a pH of about 1 to about 5, e.g., about 1 to about 4.5, about 1 to about 4, about 1 to about 3.5, about 1 to about 3, about 1 to about 2.5, or about 1 to about 2.

The polishing composition optionally comprises a mineral acid. Non-limiting examples of suitable mineral acids include nitric acid, sulfuric acid, and phosphoric acid.

The polishing composition can further comprise a base to adjust the pH of the polishing composition. Non-limiting examples of suitable bases include sodium hydroxide, potassium hydroxide, and ammonium hydroxide.

The polishing composition can be prepared by any suitable technique, many of which are known to those skilled in the art. The polishing composition can be prepared in a batch or continuous process. Generally, the polishing composition can be prepared by combining the components thereof in any order. The term “component” as used herein includes individual ingredients (e.g., colloidal silica, fused silica, compound of formula (I) or combination of compound of formula (II) and hydrophobic organic compound, amino acid, hydrogen peroxide, etc.) as well as any combination of ingredients (e.g., colloidal silica, fused silica, compound of formula (I) or combination of compound of formula (II) and hydrophobic organic compound, amino acid, hydrogen peroxide, etc.).

For example, the colloidal silica and fused silica can be dispersed in water. The compound of formula (I) or combination of compound of formula (II) and hydrophobic organic compound and amino acid can then be added, and mixed by any method that is capable of incorporating the components into the polishing composition. The hydrogen peroxide can be added at any time during the preparation of the polishing composition. The polishing composition can be prepared prior to use, with one or more components, such as the hydrogen peroxide, added to the polishing composition just before use (e.g., within about 1 minute before use, or within about 1 hour before use, or within about 7 days before use). The polishing composition also can be prepared by mixing the components at the surface of the substrate during the polishing operation.

The polishing composition can be supplied as a one-package system comprising colloidal silica, fused silica, compound of formula (I) or combination of compound of formula (II) and hydrophobic organic compound, amino acid, and water. Alternatively, the colloidal silica and fused silica can be supplied as a dispersion in water in a first container, and compound of formula (I) or combination of compound of formula (II) and hydrophobic organic compound, amino acid can be supplied in a second container, either in dry form, or as a solution or dispersion in water. The hydrogen peroxide desirably is supplied separately from the other components of the polishing composition and is combined, e.g., by the end-user, with the other components of the polishing composition shortly before use (e.g., 1 week or less prior to use, 1 day or less prior to use, 1 hour or less prior to use, 10 minutes or less prior to use, or 1 minute or less prior to use). The components in the first or second container can be in dry form while the components in the other container can be in the form of an aqueous dispersion. Moreover, it is suitable for the components in the first and second containers to have different pH values, or alternatively to have substantially similar, or even equal, pH values. Other two-container, or three or more-container, combinations of the components of the polishing composition are within the knowledge of one of ordinary skill in the art.

The polishing composition of the invention also can be provided as a concentrate which is intended to be diluted with an appropriate amount of water prior to use. In such an embodiment, the polishing composition concentrate can comprise the colloidal silica, fused silica, compound of formula (I) or combination of compound of formula (II) and hydrophobic organic compound, amino acid, and water, with or without the hydrogen peroxide, in amounts such that, upon dilution of the concentrate with an appropriate amount of water, and upon addition of the hydrogen peroxide if not already present in an appropriate amount, each component of the polishing composition will be present in the polishing composition in an amount within the appropriate range recited above for each component. For example, the colliodal silica, fused silica, compound of formula (I) or combination of compound of formula (II) and hydrophobic organic compound, and amino acid can each be present in the concentration in an amount that is about 2 times (e.g., about 3 times, about 4 times, or about 5 times) greater than the concentration recited above for each component so that, when the concentrate is diluted with an equal volume of (e.g., 2 equal volumes of water, 3 equal volumes of water, or 4 equal volumes of water, respectively), along with the hydrogen peroxide in a suitable amount, such that each component will be present in the polishing composition in an amount within the ranges set forth above for each component. Furthermore, as will be understood by those of ordinary skill in the art, the concentrate can contain an appropriate fraction of the water present in the final polishing composition in order to ensure that other components are at least partially or fully dissolved in the concentrate.

The invention also provides a method of chemically mechanically polishing a substrate comprising (i) providing a substrate, (ii) providing a polishing pad, (iii) providing a chemical-mechanical polishing composition as described herein, (iv) contacting the substrate with the polishing pad and the chemical-mechanical polishing composition, and (v) moving the polishing pad and the chemical mechanical polishing composition relative to the substrate to abrade at least a portion of a surface of the substrate to thereby polish the substrate

The substrate to be polished using the method of the invention can be any suitable substrate, especially a substrate that contains nickel-phosphorous. A preferred substrate comprises at least one layer on a surface of the substrate, especially an exposed layer for polishing, comprising, consisting essentially of, or consisting of nickel-phosphorous, such that at least a portion of the nickel-phosphorous on a surface of the substrate is abraded (i.e., removed) to polish the substrate. Particularly suitable substrates include, but are not limited to, memory or rigid disks, such as aluminum disks coated with nickel-phosphorous. A preferred substrate is a nickel-phosphorous-coated aluminum memory disk.

The polishing method of the invention is particularly suited for use in conjunction with a chemical-mechanical polishing (CMP) apparatus. Typically, the apparatus comprises a platen, which, when in use, is in motion and has a velocity that results from orbital, linear, or circular motion, a polishing pad in contact with the platen and moving with the platen when in motion, and a carrier that holds a substrate to be polished by contacting and moving relative to the surface of the polishing pad. The polishing of the substrate takes place by the substrate being placed in contact with the polishing pad and the polishing composition of the invention and then the polishing pad moving relative to the substrate, so as to abrade at least a portion of the substrate to polish the substrate.

A substrate can be planarized or polished with the chemical-mechanical polishing composition with any suitable polishing pad (e.g., polishing surface). Suitable polishing pads include, for example, woven and non-woven polishing pads. Moreover, suitable polishing pads can comprise any suitable polymer of varying density, hardness, thickness, compressibility, ability to rebound upon compression, and compression modulus. Suitable polymers include, for example, polyvinylchloride, polyvinylfluoride, nylon, fluorocarbon, polycarbonate, polyester, polyacrylate, polyether, polyethylene, polyamide, polyurethane, polystyrene, polypropylene, coformed products thereof, and mixtures thereof.

Desirably, the CMP apparatus further comprises an in situ polishing endpoint detection system, many of which are known in the art. Techniques for inspecting and monitoring the polishing process by analyzing light or other radiation reflected from a surface of the workpiece are known in the art. Such methods are described, for example, in U.S. Pat. Nos. 5,196,353, 5,433,651, 5,609,511, 5,643,046, 5,658,183, 5,730,642, 5,838,447, 5,872,633, 5,893,796, 5,949,927, and 5,964,643. Desirably, the inspection or monitoring of the progress of the polishing process with respect to a workpiece being polished enables the determination of the polishing end-point, i.e., the determination of when to terminate the polishing process with respect to a particular workpiece.

Desirably, the inventive polishing composition exhibits decreased roll-off as compared with conventional polishing compositions. In particular, the inventive polishing composition exhibits decreased XRC (extreme radius of curvature) and decreased XRCE (extreme radius of curvature at the extreme edge of the disk) as measured by an optical profilometer.

The invention can be characterized by the following embodiments.

EMBODIMENTS

(1) In embodiment (1) is presented a chemical-mechanical polishing composition comprising (a) an abrasive comprising colloidal silica and fused silica, (b) about 10 ppm to about 1000 ppm of a compound of formula (I):

wherein R is selected from

a straight chain or branched chain C₁-C₂₀ alkyl,

and

R⁵C₆H₄, and

R⁶—O—(R⁷O)_(n)—,

wherein R¹-R⁵ are independently selected from straight chain or branched chain C₁-C₂₀ alkyls,

wherein R⁶ is a straight chain or branched chain C₁-C₂₀ alkyl or R⁸—C₆H₄—,

wherein R⁷ is a straight chain or branched chain C₂-C₁₀ alkylene,

wherein R⁸ is a straight chain or branched chain C₁-C₂₀ alkyl,

wherein n is an integer of from 1 to about 20,

wherein X and Y are independently O or a covalent bond, and

wherein A and B are independently an alkali metal cation or an organic amine compound, (c) an amino acid, (d) hydrogen peroxide, and (e) water, wherein the polishing composition has a pH of about 1 to about 5,

(2) In embodiment (2) is presented the polishing composition of embodiment (1), wherein the colloidal silica has an average particle size of about 10 nm to about 200 nm.

(3) In embodiment (3) is presented the polishing composition of embodiment (1) or (2), wherein the fused silica has an average particle size of about 100 nm to about 800 nm.

(4) In embodiment (4) is presented the polishing composition of any one of embodiments (1)-(3), wherein the compound of formula (I) is selected from sodium dodecyl sulfate, diethylhexyl sulfosuccinate, dodecylbenzene sulfonate, a sec-alkyl derivative of benzenesulfonic acid, an alkyl diphenyloxide disulfonate, secondary alkane sulfonate, mono alkyl branched propoxy sulfate, polyethyleneglycol nonylphenyl ether sulfate and combinations thereof.

(5) In embodiment (5) is presented the polishing composition of any one of embodiments (1)-(4), wherein the amino acid is glycine or alanine.

(6) In embodiment (6) is presented the polishing composition of any one of embodiments (1)-(5), wherein the polishing composition comprises about 100 ppm to about 500 ppm of the compound of formula (I).

(7) In embodiment (7) is presented the polishing composition of any one of embodiments (1)-(6), wherein the polishing composition comprises about 0.1 wt. % to about 10 wt. % of a combination of colloidal silica and fused silica.

(8) In embodiment (8) is presented a method of chemically mechanically polishing a substrate comprising (i) providing a substrate, (ii) providing a polishing pad, (iii) providing a chemical-mechanical polishing composition of any one of embodiments (1)-(7), (iv) contacting the substrate with the polishing pad and the chemical-mechanical polishing composition, and (v) moving the polishing pad and the chemical mechanical polishing composition relative to the substrate to abrade at least a portion of a surface of the substrate to thereby polish the substrate.

(9) In embodiment (9) is presented the method of embodiment (8), wherein the substrate is a nickel-phosphorous-coated aluminum memory disk, wherein the substrate comprises nickel-phosphorous on a surface of the substrate, and wherein at least a portion of the nickel-phosphorous on a surface of the substrate is abraded to polish the substrate.

(10) In embodiment (10) is presented a chemical-mechanical polishing composition comprising (a) an abrasive comprising colloidal silica and fused silica, (b) a compound of formula (II):

wherein R⁹ is H or a hydroxyalkyl, and wherein m is an integer of from 2 to about 6, (c) a hydrophobic organic compound selected from an aryloxy alcohol, a diester, and a triester, (d) hydrogen peroxide, (e) an amino acid, and (f) water, wherein the polishing composition has a pH of about 1 to about 5.

(11) In embodiment (11) is presented the polishing composition of embodiment (10), wherein the colloidal silica has an average particle size of about 10 nm to about 200 nm.

(12) In embodiment (12) is presented the polishing composition of embodiment (10) or (11), wherein the fused silica has an average particle size of about 100 nm to about 800 nm.

(13) In embodiment (13) is presented the polishing composition of any one of embodiments (10)-(12), wherein the compound of formula (II) is ethylenediamine or hydroxyethylethylenediamine.

(14) In embodiment (14) is presented the polishing composition of any one of embodiments (10)-(13), wherein the hydrophobic organic compound is phenoxyethanol.

(15) In embodiment (15) is presented the polishing composition of any one of embodiments (10)-(14), wherein the hydrophobic organic compound is triethyl citrate.

(16) In embodiment (16) is presented the polishing composition of any one of embodiments (10)-(15), wherein the polishing composition comprises about 100 ppm to about 3000 ppm of a combination of the compound of formula (II) and the hydrophobic organic compound.

(17) In embodiment (17) is presented the polishing composition of any one of embodiments (10)-(16), wherein the amino acid is glycine or alanine.

(18) In embodiment (18) is presented the polishing composition of any one of embodiments (10)-(17), wherein the polishing composition comprises about 0.1 wt. % to about 10 wt. % of a combination of colloidal silica and fused silica.

(19) In embodiment (19) is presented a method of chemically mechanically polishing a substrate comprising (i) providing a substrate, (ii) providing a polishing pad, (iii) providing the chemical-mechanical polishing composition of any one of embodiments (10)-(18), (iv) contacting the substrate with the polishing pad and the chemical-mechanical polishing composition, and (v) moving the polishing pad and the chemical mechanical polishing composition relative to the substrate to abrade at least a portion of a surface of the substrate to thereby polish the substrate.

(20) In embodiment (20) is presented the method of embodiment (19), wherein the substrate is a nickel-phosphorous-coated aluminum memory disk, wherein the substrate comprises nickel-phosphorous on a surface of the substrate, and wherein at least a portion of the nickel-phosphorous on a surface of the substrate is abraded to polish the substrate.

EXAMPLES

The following examples further illustrate the invention but, of course, should not be construed as in any way limiting its scope.

In the examples that follow, nickel-phosphorus-coated aluminum disks were polished with a Ceiba CR200™ polishing pad using a Speedfam™ 16B polisher (Konegawa, Japan). Twenty (20) disks were polished in each run at a slurry flow rate of 550 mL/min to a target NiP removal amount of 150±5 mg. After polishing, the disks were cleaned in an ultrasonic bath using a cleaning solution, and then dried. Edge roll-off measurements XRC (extreme radius of curvature) and XRCE (extreme radius of curvature at the extreme edge of the disk) were determined using a Zygo Newview™ 100 (Middlefield, Conn.) at 80-600 μm wavelength. Two disks from each run were measured at 1200, 240°, and 360° of the disk (double-sided), respectively. Lower XRC/XRCE values indicate lesser edge roll-off.

All of the polishing compositions comprised a base formulation comprising 0.8 wt. % fused silica having an average particle size of 0.45 μm (i.e., 450 nm), 3.4 wt. % of colloidal silica having an average particle size of 110 nm, 0.8 wt. % of colloidal silica having an average particle size of 70 nm, 0.2 wt. % of glycine, 1.2 wt. % of hydrogen peroxide, and 1.6 wt. % of phosphoric acid, with the balance (92%) as deionized water. The pH of the polishing compositions at the point-of-use was 1.5±0.1.

Example 1

This example demonstrates the effect of addition of a compound of formula (I) on the XRC and XRCE exhibited by the base formulation, in accordance with an embodiment of the invention.

Nickel-phosphorus-coated aluminum disks were polished with Polishing Compositions 1A-1I. Polishing Composition 1A (control) was the base formulation and did not contain a compound of formula (I). Polishing Compositions 1B-1I (inventive) included the base formulation and further contained a compound of formula (I) of the type and in the amount shown in Table 1.

Following polishing, the XRC and XRCE were determined, and the results are set forth in Table 1.

TABLE 1 Effect of a Compound of Formula (I) on XRC and XRCE Amount of Compound of Polishing Compound Formula (I) XRC XRCE Composition of Formula (I) (ppm) (nm) (nm) 1A (control) — 0 34.7 222.3 1B Sodium dodecyl sulfate 250 31.0 182.0 1C Diethylhexyl 300 24.0 193.4 sulfosuccinate 1D Dodecylbenzene sulfonate 300 21.9 140.1 1E Dodecylbenzene 300 21.2 165.0 sulfonate-Isopropylamine Salt 1F Benzenesulfonic acid 300 18.7 157.8 C₁₀-C₁₃ sec-alkyl derivative-Isopropylamine Salt 1G Diphenyloxide disulfonate 300 25.4 164.5 C₁₀-alkyl derivative 1H Diphenyloxide disulfonate 300 19.1 195.6 C₁₀-alkyl derivative (Dowfax ™ C10L) 1I Diphenyloxide disulfonate 300 20.5 140.1 C₁₀-alkyl derivative 1J Poly(oxy-1,2-ethanediyl), 200 24.0 153.4 a-sulfo-w- (nonylphenoxy)-, branched, ammonium salt 1K Isotridecanol propoxylated 400 29.2 166.7 sulfated monoisopropanolamine adduct 1L Dodecane-l-ol 400 25.0 162.3 propoxylated sulfated monoisopropanolamine adduct 1M 2-Butyl-octane-l-ol 400 25.3 180.0 propoxylated sulfated monoisopropanolamine adduct 1N C14/16-alpha olefin 200 22.2 153.4 sulphonate sodium salt 1O C14/C17 Secondary 200 15.6 153.3 alkane sulfonate

As is apparent from the results set forth in Table 1, nickel-phosphorus-coated aluminum disks polished with Polishing Compositions 1B-10, which contained a compound of formula (I), exhibited XRC and XRCE values that were substantially lower than the XRC and XRCE values exhibited by disks polished with the control composition that did not contain a compound of formula (I). In particular, the XRC values exhibited by disks polished with polishing compositions including a compound of formula (I) were approximately 59-89% of the XRC values exhibited by disks polished with the control polishing composition, and the XRCE values exhibited by disks polished with polishing compositions including a compound of formula (I) were approximately 63-82% of the XRCE values exhibited by disks polished with the control polishing composition.

Example 2

This example demonstrates the effect of increasing the concentration of a compound of formula (I) on the XRC and XRCE values exhibited by nickel-phosphorus-coated aluminum disks polished with a polishing composition comprising a compound of formula (I), in accordance with an embodiment of the invention.

Nickel-phosphorus-coated aluminum disks were polished with Polishing Compositions 1A and 2A-2C. Polishing Composition 1A (control) was the base formulation and did not contain a compound of formula (I). Polishing Compositions 2A-2C (inventive) included the base formulation and further contained 250 ppm, 375 ppm, and 500 ppm, respectively, of sodium dodecyl sulfate (i.e., a compound of formula (I)).

Following polishing, the XRC and XRCE were determined, and the results are set forth in Table 2.

TABLE 2 Effect of Concentration of Sodium Dodecyl Sulfate on XRC and XRCE Amount of Sodium Polishing Dodecyl Sulfate XRC XRCE Composition (ppm) (nm) (nm) 1A (control) 0 34.7 222.3 2A 250 31.0 182.0 2B 375 27.8 155.6 2C 500 25.0 152.0

As is apparent from the results set forth in Table 2, the XRC and XRCE exhibited by nickel-phosphorus-coated aluminum disks polished with polishing compositions containing sodium dodecyl sulfate decreased with increasing concentration of sodium dodecyl sulfate, with the decrease in XRCE appearing to plateau between 375 and 500 ppm of sodium dodecyl sulfate.

Example 3

This example demonstrates the effect of increasing the concentration of a compound of formula (I) on the XRC and XRCE values exhibited by nickel-phosphorus-coated aluminum disks polished with a polishing composition comprising a compound of formula (I), in accordance with an embodiment of the invention.

Nickel-phosphorus-coated aluminum disks were polished with Polishing Compositions 1A and 3A-3D. Polishing Composition 1A (control) was the base formulation and did not contain a compound of formula (I). Polishing Compositions 3A-3D (inventive) included the base formulation and further contained 150 ppm, 300 ppm, 450 ppm, and 600 ppm, respectively, of diethylhexyl sulfosuccinate (i.e., a compound of formula (I)).

Following polishing, the XRC and XRCE were determined, and the results are set forth in Table 3.

Table 3 Effect of Concentration of Diethylhexyl Sulfosuccinate on XRC and XRCE Amount of Diethylhexyl Polishing Sulfosuccinate XRC XRCE Composition (ppm) (nm) (nm) 1A (control) 0 34.7 222.3 3A 150 31.3 206.7 3B 300 24.0 19.4 3C 450 20.4 162.3 3D 600 20.0 159.0

As is apparent from the results set forth in Table 3, the XRC and XRCE exhibited by nickel-phosphorus-coated aluminum disks polished with polishing compositions containing diethylhexyl sulfosuccinate decreased with increasing concentration of diethylhexyl sulfosuccinate up to 450 ppm, with the decrease in XRC and XRCE appearing to plateau between 450 and 600 ppm of diethylhexyl sulfosuccinate.

Example 4

This example demonstrates the effect of increasing the concentration of a compound of formula (I) on the XRC and XRCE values exhibited by nickel-phosphorus-coated aluminum disks polished with a polishing composition comprising a compound of formula (I), in accordance with an embodiment of the invention.

Nickel-phosphorus-coated aluminum disks were polished with Polishing Compositions 1A and 4A-4C. Polishing Composition 1A (control) was the base formulation and did not contain a compound of formula (I). Polishing Compositions 4A-4C (inventive) included the base formulation and further contained 200 ppm, 400 ppm, and 600 ppm, respectively, of dodecylbenzene sulfonate (i.e., a compound of formula (I)).

Following polishing, the XRC and XRCE were determined, and the results are set forth in Table 4.

Table 4 Effect of Concentration of Dodecylbenzene Sulfonate on XRC and XRCE Amount of Dodecylbenzene Polishing Sulfonate XRC XRCE Composition (ppm) (nm) (nm) 1A (control) 0 34.7 222.3 4A 200 21.2 164.5 4B 400 14.2 137.8 4C 600 17.0 146.7

As is apparent from the results set forth in Table 4, the XRC and XRCE exhibited by nickel-phosphorus-coated aluminum disks polished with polishing compositions containing dodecylbenzene sulfonate decreased with increasing concentration of dodecylbenzene sulfonate up to 400 ppm, with the decrease in XRC and XRCE appearing to plateau between 400 and 600 ppm of dodecylbenzene sulfonate.

Example 5

This example demonstrates the effect of increasing the concentration of a compound of formula (I) on the XRC and XRCE values exhibited by nickel-phosphorus-coated aluminum disks polished with a polishing composition comprising a compound of formula (I), in accordance with an embodiment of the invention.

Nickel-phosphorus-coated aluminum disks were polished with Polishing Compositions 1A and 5A-5C. Polishing Composition 1A (control) was the base formulation and did not contain a compound of formula (I). Polishing Compositions 5A-5C (inventive) included the base formulation and further contained 200 ppm, 300 ppm, and 400 ppm, respectively, of dodecylbenzene sulfonate-isopropylamine salt (i.e., a compound of formula (I)).

Following polishing, the XRC and XRCE were determined, and the results are set forth in Table 5.

TABLE 5 Effect of Concentration of Dodecylbenzene Sulfonate- Isopropylamine Salt on XRC and XRCE Amount of Dodecylbenzene Sulfonate-Isopropylamine Polishing Salt XRC XRCE Composition (ppm) (nm) (nm) 1A (control) 0 34.7 222.3 5A 200 22.9 170.0 5B 300 21.2 164.5 5C 400 20.5 162.3

As is apparent from the results set forth in Table 5, the XRC and XRCE exhibited by nickel-phosphorus-coated aluminum disks polished with polishing compositions containing dodecylbenzene sulfonate-isopropylamine salt decreased with increasing concentration of dodecylbenzene sulfonate-isopropylamine salt up to 300 ppm, with the decrease in XRC and XRCE appearing to plateau between 300 and 400 ppm of dodecylbenzene sulfonate-isopropylamine salt.

Example 6

This example demonstrates the effect of increasing the concentration of a compound of formula (I) on the XRC and XRCE values exhibited by nickel-phosphorus-coated aluminum disks polished with a polishing composition comprising a compound of formula (I), in accordance with an embodiment of the invention.

Nickel-phosphorus-coated aluminum disks were polished with Polishing Compositions 1A and 6A-6C. Polishing Composition 1A (control) was the base formulation and did not contain a compound of formula (I). Polishing Compositions 6A-6C (inventive) included the base formulation and further contained 200 ppm, 300 ppm, and 400 ppm, respectively, of benzenesulfonic acid C₁₀-C₁₃ sec-alkyl derivative isopropylamine salt (i.e., a compound of formula (I)).

Following polishing, the XRC and XRCE were determined, and the results are set forth in Table 6.

TABLE 6 Effect of Concentration of Benzenesulfonic Acid C₁₀-C₁₃ Sec-Alkyl Derivative-Isopropylamine Salt on XRC and XRCE Amount of Benzenesulfonic Acid C₁₀-C₁₃ Sec-Alkyl Derivative- Polishing Isopropylamine Salt XRC XRCE Composition (ppm) (nm) (nm) 1A (control) 0 34.7 222.3 6A 200 23.7 162.3 6B 300 18.7 157.8 6C 400 18.9 155.6

As is apparent from the results set forth in Table 6, the XRC and XRCE exhibited by nickel-phosphorus-coated aluminum disks polished with polishing compositions containing benzenesulfonic acid C₁₀-C₁₃ sec-alkyl derivative-isopropylamine salt decreased with increasing concentration of benzenesulfonic acid C₁₀-C₁₃ sec-alkyl derivative-isopropylamine salt up to 300 ppm, with the decrease in XRC and XRCE appearing to plateau between 300 and 400 ppm of benzenesulfonic acid C₁₀-C₁₃ sec-alkyl derivative-isopropylamine salt.

Example 7

This example demonstrates the effect of increasing the concentration of a compound of formula (I) on the XRC and XRCE values exhibited by nickel-phosphorus-coated aluminum disks polished with a polishing composition comprising a compound of formula (I), in accordance with an embodiment of the invention.

Nickel-phosphorus-coated aluminum disks were polished with Polishing Compositions 1A and 7A-7H. Polishing Composition 1A (control) was the base formulation and did not contain a compound of formula (I). Polishing Compositions 7A-7C (inventive) included the base formulation and further contained 200 ppm, 300 ppm, and 400 ppm, respectively, of diphenyloxide disulfonate C₁₀-alkyl derivative (i.e., a compound of formula (I)). Polishing Compositions 7D and 7E (inventive) included the base formulation and further contained 300 ppm and 400 ppm, respectively, of the diphenyloxide disulfonate C₁₀-alkyl derivative Dowfax™ C10L (i.e., a compound of formula (I)). Polishing Compositions 7F-7H (inventive) included the base formulation and further contained 200 ppm, 300 ppm, and 400 ppm, respectively, of diphenyloxide disulfonate C₁₂-alkyl derivative (i.e., a compound of formula (I)).

Following polishing, the XRC and XRCE were determined, and the results are set forth in Table 7.

TABLE 7 Effect of Diphenyl Disulfonates on XRC and XRCE Amount of Compound of Polishing Compound of Formula (I) XRC XRCE Composition Formula (I) (ppm) (nm) (nm) 1A (control) — 0 34.7 222.3 7A Diphenyloxide 200 25.4 164.5 7B disulfonate 300 18.1 158.2 7C C₁₀-alkyl derivative 400 16.3 136.0 7D Diphenyloxide 300 19.1 195.6 7E disulfonate 400 18.4 157.8 C₁₀-alkyl (Dowfax ™ C10L) 7F Diphenyloxide 200 27.8 186.4 7G disulfonate 300 20.5 140.0 7H C₁₂-alkyl 400 21.2 141.0 derivative

As is apparent from the results set forth in Table 7, the presence of diphenyloxide disulfonate compounds in Polishing Compositions 7A-7H resulted in decreased XRC and XRCE observed in nickel-phosphorus-coated aluminum disks polished using the same.

Example 8

This example demonstrates the effect of a combination of a compound of formula (II) and a hydrophobic organic compound on the XRC and XRCE values exhibited by nickel-phosphorus-coated aluminum disks polished with a polishing composition comprising a compound of formula (II) and a hydrophobic organic compound, in accordance with an embodiment of the invention.

Nickel-phosphorus-coated aluminum disks were polished with Polishing Compositions 1A and 8A-8G. Polishing Composition 1A (control) was the base formulation and did not contain a compound of formula (II), a hydrophobic organic compound, or a compound of formula (I). Polishing Compositions 8A-8G included the base formulation and further contained 600 ppm of ethylenediamine (i.e., a compound of formula (II)) (Polishing Composition 8A), 1000 ppm of hydroxyethylethylenediamine (i.e., a compound of formula (II)) (Polishing Composition 8B), 2000 ppm of phenoxyethanol (i.e., a hydrophobic organic compound) (Polishing Composition 8C), 600 ppm of ethylenediamine and 2000 ppm of phenoxyethanol (Polishing Composition 8D), 2000 ppm of triethyl citrate (i.e., a hydrophobic organic compound) (Polishing Composition 8E), 600 ppm of ethylenediamine and 2000 ppm of triethyl citrate (Polishing Composition 8F), or 1557 ppm of hydroxyethylethylenediamine and 2000 ppm of triethyl citrate (Polishing Composition 8G).

Following polishing, the XRC and XRCE were determined, and the results are set forth in Table 8.

TABLE 8 Effect of the Combination of a Compound of Formula (II) and a Hydrophobic Organic Compound on XRC and XRCE Hydrophobic Compound of Organic Polishing Formula (II) Compound Composition (ppm) (ppm) XRC (nm) XRCE (nm) 1A — — 34.7 222.3 (control) 8A 600 ppm — 30.9 197.9 (comparative) Ethylenediamine 8B 1000 pppm — 32.3 200.1 (comparative) Hydroxy- ethylenediamine 8C — 2000 ppm 32.3 209.0 (comparative) Phenoxyethanol 8D 600 ppm 2000 ppm 27.1 186.7 (inventive) Ethylenediamine Phenoxyethanol 8E — 2000 ppm 29.9 204.5 (comparative) Triethyl Citrate 8F 600 ppm 2000 ppm 23.6 181.0 (inventive) Ethylenediamine Triethyl Citrate 8G 1557 ppm 2000 ppm 29.2 162.3 (inventive) Hydroxy- Triethyl Citrate ethylenediamine

As is apparent from the results set forth in Table 8, the presence of ethylenediamine, hydroxyethylethylenediamine, phenoxyethanol, or triethyl citrate alone, i.e., a compound of formula (II) alone or a hydrophobic organic compound alone (as in Polishing Compositions 8A, 8B, 8C, and 8E), resulted in a modest decrease in XRCE. The presence of a combination of ethylenediamine and phenoxyethanol, ethylenediamine and triethyl citrate, or hydroxyethylethylenediamine and triethyl citrate, i.e., the combination of a compound of formula (II) and a hydrophobic organic compound (as in Polishing Compositions 8D, 8F, and 8G), resulted in a significant decrease in XRCE. For example, Polishing Composition 8D, which contained a combination of ethylenediamine and phenoxyethanol, exhibited an approximately 5.6% lower XRCE than did Polishing Composition 8A, which contained ethylenediamine but did not further contain phenoxyethanol. Polishing Composition 8G, which contained a combination of hydroxyethylethylenediamine and triethyl citrate, exhibited an approximately 19% lower XRCE than did Polishing Composition 8B, which contained hydroxyethylethylenediamine but did not further contain triethyl citrate. Polishing Composition 8D, which contained a combination of ethylenediamine and phenoxyethanol, exhibited an approximately 11% lower XRCE than did Polishing Composition 8C, which contained phenoxyethanol but did not further contain ethylenediamine. Polishing Composition 8F, which contained a combination of ethylenediamine and triethyl citrate, exhibited an approximately 12% lower XRCE than did Polishing Composition 8E, which contained triethyl citrate but did not further contain ethylenediamine. Polishing Composition 8G, which contained a combination of hydroxyethylethylenediamine and triethyl citrate, exhibited an approximately 21% lower XRCE than did Polishing Composition 8E, which contained triethyl citrate but did not further contain hydroxyethylethylenediamine.

All references, including publications, patent applications, and patents, cited herein are hereby incorporated by reference to the same extent as if each reference were individually and specifically indicated to be incorporated by reference and were set forth in its entirety herein.

The use of the terms “a” and “an” and “the” and “at least one” and similar referents in the context of describing the invention (especially in the context of the following claims) are to be construed to cover both the singular and the plural, unless otherwise indicated herein or clearly contradicted by context. The use of the term “at least one” followed by a list of one or more items (for example, “at least one of A and B”) is to be construed to mean one item selected from the listed items (A or B) or any combination of two or more of the listed items (A and B), unless otherwise indicated herein or clearly contradicted by context. The terms “comprising,” “having,” “including,” and “containing” are to be construed as open-ended terms (i.e., meaning “including, but not limited to,”) unless otherwise noted. Recitation of ranges of values herein are merely intended to serve as a shorthand method of referring individually to each separate value falling within the range, unless otherwise indicated herein, and each separate value is incorporated into the specification as if it were individually recited herein. All methods described herein can be performed in any suitable order unless otherwise indicated herein or otherwise clearly contradicted by context. The use of any and all examples, or exemplary language (e.g., “such as”) provided herein, is intended merely to better illuminate the invention and does not pose a limitation on the scope of the invention unless otherwise claimed. No language in the specification should be construed as indicating any non-claimed element as essential to the practice of the invention.

Preferred embodiments of this invention are described herein, including the best mode known to the inventors for carrying out the invention. Variations of those preferred embodiments may become apparent to those of ordinary skill in the art upon reading the foregoing description. The inventors expect skilled artisans to employ such variations as appropriate, and the inventors intend for the invention to be practiced otherwise than as specifically described herein. Accordingly, this invention includes all modifications and equivalents of the subject matter recited in the claims appended hereto as permitted by applicable law. Moreover, any combination of the above-described elements in all possible variations thereof is encompassed by the invention unless otherwise indicated herein or otherwise clearly contradicted by context. 

The invention claimed is:
 1. A chemical-mechanical polishing composition comprising: (a) an abrasive comprising colloidal silica and fused silica, (b) about 10 ppm to about 1000 ppm of a compound of formula (I):

wherein R is selected from a straight chain or branched chain C₁-C₂₀ alkyl,

R⁵C₆H₄, and R⁶—O—(R⁷O)_(n)—, wherein R¹-R⁵ are independently selected from straight chain or branched chain C₁-C₂₀ alkyls, wherein R⁶ is a straight chain or branched chain C₁-C₂₀ alkyl or R⁸—C₆H₄—, wherein R⁷ is a straight chain or branched chain C₂-C₁₀ alkylene, wherein R⁸ is a straight chain or branched chain C₁-C₂₀ alkyl, wherein n is an integer of from 1 to about 20, wherein X and Y are independently O or a covalent bond, and wherein A and B are independently an alkali metal cation or an organic amine compound, (c) an amino acid, (d) hydrogen peroxide, and (e) water, wherein the polishing composition has a pH of about 1 to about
 5. 2. The polishing composition of claim 1, wherein the colloidal silica has an average particle size of about 10 nm to about 200 nm.
 3. The polishing composition of claim 1, wherein the fused silica has an average particle size of about 100 nm to about 800 nm.
 4. The polishing composition of claim 1, wherein the compound of formula (I) is selected from sodium dodecyl sulfate, diethylhexyl sulfosuccinate, dodecylbenzene sulfonate, a sec-alkyl derivative of benzenesulfonic acid, an alkyl diphenyloxide disulfonate, secondary alkane sulfonate, mono alkyl branched propoxy sulfate, polyethyleneglycol nonylphenyl ether sulfate and combinations thereof.
 5. The polishing composition of claim 1, wherein the amino acid is glycine or alanine.
 6. The polishing composition of claim 1, wherein the polishing composition comprises about 100 ppm to about 500 ppm of the compound of formula (I).
 7. The polishing composition of claim 1, wherein the polishing composition comprises about 0.1 wt. % to about 10 wt. % of a combination of colloidal silica and fused silica.
 8. A method of chemically mechanically polishing a substrate comprising: (i) providing a substrate, (ii) providing a polishing pad, (iii) providing the chemical-mechanical polishing composition of claim 1, (iv) contacting the substrate with the polishing pad and the chemical-mechanical polishing composition, and (v) moving the polishing pad and the chemical mechanical polishing composition relative to the substrate to abrade at least a portion of a surface of the substrate to thereby polish the substrate.
 9. The method of claim 8, wherein the substrate is a nickel-phosphorous-coated aluminum memory disk, wherein the substrate comprises nickel-phosphorous on a surface of the substrate, and wherein at least a portion of the nickel-phosphorous on a surface of the substrate is abraded to polish the substrate. 